This MedLibrary.org supplementary page on Linear low-density polyethylene is provided directly from the open source Wikipedia as a service to our readers. Please see the note below on authorship of this content, as well as the Wikipedia usage guidelines. To search for other content from our encyclopedia supplement, please use the form below:
Related Sponsors
Linear low-density polyethylene (LLDPE) is a substantially linear polymer (polyethylene), with significant numbers of short branches, commonly made by copolymerization of ethylene with longer-chain olefins. Linear low-density polyethylene differs structurally from conventional low-density polyethylene because of the absence of long chain branching. The linearity of LLDPE results from the different manufacturing processes of LLDPE and LDPE. In general, LLDPE is produced at lower temperatures and pressures by copolymerization of ethylene and such higher alpha olefins as butene, hexene, or octene. The copolymerization process produces an LLDPE polymer that has a narrower molecular weight distribution than conventional LDPE and in combination with the linear structure, significantly different rheological properties.
Contents |
Production and properties
The production of LLDPE is initiated by transition metal catalysts, particularly Ziegler or Philips type of catalyst. The actual polymerization process can be done in either solution phase or gas phase reactors. Usually, octene is the copolymer in solution phase while butene and hexene are copolymerized with ethylene in a gas phase reactor. The LLDPE resin produced in a gas phase reactor is in granular form and may be sold as granules or processed into pellets. LLDPE has higher tensile strength and higher impact and puncture resistance than LDPE. It is very flexible and elongates under stress. It can be used to make thinner films, with better environmental stress cracking resistance. It has good resistance to chemicals and to ultraviolet radiation. It has good electrical properties. However it is not as easy to process as LDPE, has lower gloss, and narrower range for heat sealing.
Processing
LDPE and LLDPE have unique theoretical or melt flow properties. LLDPE is less shear sensitive because of its narrower molecular weight distribution and shorter chain branching. During a shearing process, such as extrusion, LLDPE remains more viscous, therefore harder to process than an LDPE of equivalent melt index. The lower shear sensitivity of LLDPE allows for a faster stress relaxation of the polymer chains during extrusion and therefore the physical properties are susceptible to changes in blow-up ratios. In melt extension, LLDPE has lower viscosity at all strain rates. This means it will not strain harden the way LDPE does when elongated. As the deformation rate of the polyethylene increases, LDPE demonstrates a dramatic rise in viscosity because of chain entanglement. This phenomena is not observed with LLDPE because of the lack of long-chain branching in LLDPE allows the chains to "slide by" one another upon elongation without becoming entangled. This characteristic is important for film applications because LLDPE films can be downgauged easily while maintaining high strength and toughness. The rheological properties of LLDPE are summarized as "stiff in shear" and "soft in extension
Application
LLDPE has penetrated almost all traditional markets for polyethylene, it is used for plastic bags and sheets (where it allows using lower thickness than comparable LDPE), plastic wrap, stretch wrap, pouches, toys, lids, pipes, buckets and containers, covering of cables, geomembranes, and mainly flexible tubing.
LLDPE manufactured using metallocene catalysts is labeled mLLDPE.
Physical Properties
| Property | Value |
|---|---|
| Density | 0.92 g/cm³ |
| Surface hardness | SD48 |
| Tensile strength | 20 MPa |
| Flexural modulus | 0.35 GPa |
| Notched izod | 1.06+ kJ/m |
| Linear expansion | 20×10−5/°C |
| Elongation at break | 500% |
| Strain at yield | 20% |
| Max. operating temp. | 50 °C |
| Water absorption | 0.01% |
| Oxygen index | 17% |
| Flammability UL94 | HB |
| Volume resistivity | 1016 Ω·cm |
| Dielectric strength | 25 MV/m |
| Dissipation factor 1 kHz | 909090 |
| Dielectric constant 1 kHz | 2.3 |
| HDT @ 0.45 MPa | 45 °C |
| HDT @ 1.80 MPa | 37 °C |
| Material drying | NA |
| Melting Temp. Range | 120 to 160 °C |
| Mould Shrinkage | 3% |
| Mould temp. range | 20 to 60 °C |
References:
- Modern Plastic Mid-October Encyclopedia Issue, page 56 and 61
External links
- [1] Example of LLDPE Physical Properties
See also
- Low-density polyethylene
- High-density polyethylene
- Ultra-high-molecular-weight polyethylene
- Stretch wrap
Wikipedia content modification information:
- This page was last modified on 8 January 2009, at 19:40.
Wikipedia Authorship and Review
Wikipedia content provided here is not reviewed directly by MedLibrary.org. Wikipedia content is authored by an open community of volunteers and is not produced by or in any way affiliated with MedLibrary.org.
Wikipedia Usage Guidelines
This article is licensed under the GNU Free Documentation License. It uses material from the Wikipedia article on "Linear low-density polyethylene".
The URL for this specific entry is:
All Wikipedia text is available under the terms of the GNU Free Documentation License. (See Copyrights for details). Wikipedia® is a registered trademark of the Wikimedia Foundation, Inc.