This MedLibrary.org supplementary page on Thermoset is provided directly from the open source Wikipedia as a service to our readers. Please see the note below on authorship of this content, as well as the Wikipedia usage guidelines. To search for other content from our encyclopedia supplement, please use the form below:
Related Sponsors
Thermosetting plastics thermosets) are polymer materials that irreversibly cure form. The cure may be done through heat (generally above 200 degrees Celsius), through a chemical reaction (two-part epoxy, for example), or irradiation such as electron beam processing.
Thermoset materials are usually liquid or malleable prior to curing and designed to be molded into their final form, or used as adhesives. Others are solids like that of the molding compound used in semiconductors and integrated circuits (IC's).
The curing process transforms the resin into a plastic or rubber by a cross-linking process. Energy and/or catalysts are added that cause the molecular chains to react at chemically active sites (unsaturated or epoxy sites, for example), linking into a rigid, 3-D structure. The cross-linking process forms a molecule with a larger molecular weight, resulting in a material with a higher melting point. During the reaction, the molecular weight has increased to a point so that the melting point is higher than the surrounding ambient temperature, the material forms into a solid material.
Uncontrolled reheating of the material results in reaching the decomposition temperature before the melting point is obtained. Therefore, a thermoset material cannot be melted and re-shaped after it is cured. This implies that thermosets cannot be recycled, except as filler material.1
Thermoset materials are generally stronger than thermoplastic materials due to this 3-D network of bonds, and are also better suited to high-temperature applications up to the decomposition temperature of the material.
Some examples of thermosets are:
- Polyester fiberglass systems: (SMC Sheet molding compounds and BMC Bulk molding compounds)
- Vulcanized rubber
- Bakelite, a phenol-formaldehyde resin (used in electrical insulators and plasticware)
- Duroplast, similar to Bakelite
- Urea-formaldehyde foam (used in plywood, particleboard and medium-density fibreboard)
- Melamine resin (used on worktop surfaces)
- Epoxy resin (used as an adhesive and in fibre reinforced plastics such as glass reinforced plastic and graphite-reinforced plastic)
- Polyimides (used in printed circuit boards and in body parts of modern airplanes)
- Mold or Mold Runners (the black plastic part in Integrated Circuits (IC) or semiconductors)
Some methods of molding thermosets are:
- Reactive injection molding (used for objects like milk bottle crates)
- Extrusion molding (used for making pipes, threads of fabric and insulation for electrical cables)
- Compression molding (used to shape most thermosetting plastics)
- Spin casting (used for producing fishing lures and jigs, gaming miniatures, figurines, emblems as well as production and replacement parts)
See also
References
- ^ The Open University (UK), 2000. T838 Design and Manufacture with Polymers: Introduction to Polymers, page 9. Milton Keynes: The Open University
Wikipedia content modification information:
- This page was last modified on 2 December 2008, at 18:20.
Wikipedia Authorship and Review
Wikipedia content provided here is not reviewed directly by MedLibrary.org. Wikipedia content is authored by an open community of volunteers and is not produced by or in any way affiliated with MedLibrary.org.
Wikipedia Usage Guidelines
This article is licensed under the GNU Free Documentation License. It uses material from the Wikipedia article on "Thermoset".
The URL for this specific entry is:
All Wikipedia text is available under the terms of the GNU Free Documentation License. (See Copyrights for details). Wikipedia® is a registered trademark of the Wikimedia Foundation, Inc.